나선형 침수 PTFE 침지 히터

PTFE HEATERS Features

1. High-quality stainless steel (SUS316 or SUS304) heating elements inside, 

Heavy wall PTFE covered stainless steel heating elements, strong corrosion 

resistance and applicable to all types of corrosive fluid heating.

2. Low wattage density design (10 watts/square inch, 1.5w/cm2) for longer service life.

3. Pay attention to prevent deposition from the surface of PTFE heater. 

Too thick liquid or too low liquid level will cause the breakdown of 

PTFE heater because of surface heating nonuniform.

4. Do not change the dimensions of PTFE heater smaller at random, or else

 it will make the wattage density bigger and shorten the service life. 

5. All PTFE heater can be built with overheat protection or PT100 temperature 

probe to ensure the service life and safety.

6. PTFE heater, strong corrosion-resistant, are widely used in oxidation of three polishing, chemical gold plating 

Chemical silver plating, electroless nickel plating and varieties of high demand liquid heating.

7. Flat, spiral and L-shaped,U-shaped,W-shaped,coil, portfolio configurations are available.

8. All our PTFE heater are approved by the EU market of mandatory CE Certification. 

Main reasons of breakdown of PTFE HEATERS

1. Excessively high solvent temperature

2. The presence of inhibitors

3. Too thick solvent

4. Stagnant flow of the solvent

5. Usage of forbidden potion

6. Aeration

7. Second chemical reaction because of other acids

8. Presence of oxygen or an oxidizing agent 

in the solvent

9. Grounded wrongly

10. Erosion

11. Flux floating on the surface

13. The man-made damage of PTFE surface makes 

heater not working normally.

12. The presence of undissolved gases

14. Under normal operation, the heater leaving the solvent or the liquid level lower than the heat zone